Thread: Brass importance?

As long as it has been prepped the same as all your other brass I doubt you would see any differences on paper. Especially between brass that has a couple more firings. I don't sort it. I have new loads and 5-6 times fired loads mixed in my cartridge box and they seem to perform the same accuracy and ES wise.

I don't mix brands of brass for no other reason than I always tend to buy what goes best thru my rifle and stick with it.
Neck tension and projectile consistency is more important regarding accuracy Imo.




Sent from my SM-G935F using Tapatalk

Originally Posted by R93

As long as it has been prepped the same as all your other brass I doubt you would see any differences on paper. Especially between brass that has a couple more firings. I don't sort it. I have new loads and 5-6 times fired loads mixed in my cartridge box and they seem to perform the same accuracy and ES wise.

I don't mix brands of brass for no other reason than I always tend to buy what goes best thru my rifle and stick with it.
Neck tension and projectile consistency is more important regarding accuracy Imo.




Sent from my SM-G935F using Tapatalk

I'd have to disagree.

If neck tension is important you shouldn't be mixing once fired with 5-6 fired brass as they will have quite different neck tensions.
On my 22-250 Rem, the sixth load has so little neck tension the if you de-chamber a round the bullet stays in the throat. That cartridge us a bit hotter than the 223 but you get the picture. Hard brass mixed in with soft is likely to see you getting random split necks as well. Anneal the brass every five or so (for 223, my loads probably need it every 3) firings to keep consistent neck tension.

Sent from my GT-I8190T using Tapatalk

Originally Posted by Feather or Shoot

I'd have to disagree.

If neck tension is important you shouldn't be mixing once fired with 5-6 fired brass as they will have quite different neck tensions.
On my 22-250 Rem, the sixth load has so little neck tension the if you de-chamber a round the bullet stays in the throat. That cartridge us a bit hotter than the 223 but you get the picture. Hard brass mixed in with soft is likely to see you getting random split necks as well. Anneal the brass every five or so (for 223, my loads probably need it every 3) firings to keep consistent neck tension.

Sent from my GT-I8190T using Tapatalk

(If prepped the same)

I anneal every firing. Use quality bushing dies without a button and as I said accuracy and ES are consistent from first firing till the brass is tired. Up to 8 or 9 goes on my Ackley on average.
Pretty good indication my neck tension is consistent I would have thought.

After loading a few thousand rounds you also can also feel any differences during seating and sort from there.



Sent from my SM-G935F using Tapatalk

Originally Posted by R93

(If prepped the same)

I anneal every firing. Use quality bushing dies without a button and as I said accuracy and ES are consistent from first firing till the brass is tired. Up to 8 or 9 goes on my Ackley on average.
Pretty good indication my neck tension is consistent I would have thought.

After loading a few thousand rounds you also can also feel any differences during seating and sort from there.



Sent from my SM-G935F using Tapatalk

I was wondering how you were getting consistency with mixed firing brass.
I agree, annealing every time should sort most issues. How often do you full length size? My cases start getting hard to chamber after a while. Also how do you know when to retire your brass if you have mixed firing batches?

Sent from my GT-I8190T using Tapatalk