Hi all, did my normal on lathe bullet mould making bit for a 500gr single bullet mould in ali and had a try out to see what I have got. Dropped out of the mould nicely and weight was 488grs, so not to bad, will see how they shoot with 65grs 2f in my Sharps but will be wearing my shoulder pad for sure.
Attachment 78774, Should get a kick out of my Sharps.
They look very similar to the lee 500 but with better lube grooves so should go well. Given the rifles weight, recoil should be "mild".
Is there any particular grade or series of ali used for bullet moulds? Just wondering as I have a bit of free machining ali that I could probably make something out of, but the free machining ali usually has a bit of lead and other metals alloyed with it to make it turn nicely and I wonder if that could cause issues.
Bugged if I know, I`v got a lump of ali 8' wide x .650" thick and all my moulds come form that, I`v no idea what type of ali it is so you should be ok, just smoke the mould before casting . My bullets came out .459"/ 62" dia so sized to .459" after applying lube and then loaded up some more with 37grs of 3031, should give me around 1,3200 mv in my 27" barrel. The heaver bullets are said to be good at longer ranges so will try them at 100m and 200m, that's if they shoot ok in my 1-20" twist barrel, the test is coming up.
Attachment 78788, Loaded and ready for testing. it`s just one fun thing after another.
looking great......look forward to results.
close up pic of bullets for the oldies would be appreciated . . . . R
:XD:!!,I just knew it, now I will have to explain what's the ring on the nose!!!. A bloody glitch in my nose cutter, it picked up a lump of ali and that's the result but may be ok as a bigger memplate , aww, hole , good for hunting? , may be the new bullet shape of the century at the deer cemetery . :cool:
Attachment 78793,
Attachment 78794, All will end up down range.
looks even better up close...and the nose thing...well it just looks phalic to me...like a knob with foreskin lol.....sorry it just does,bet it will shoot just as good.
Pervert !, now I`ll have to hide them away form all the girl shooter at the range, specially with my pink bullet lube, would think I`m a dirty old man. "Look at that mans bullets, don`t they look sexy" :XD:
OK, Update on the 488gr cast bullets, tried some with 3031, 35.5gr and 40gr, at 100m not good , five shots and no holes in the target. All were going over the top and when I did get some on they were all over the place, so no target. Next batch was loaded with 65gr 2f Swiss and shot at 50m , a lot better, could see where they where going and liked the black powder better. Looks like I`ll be trying the black at 100m to see if I can get a group of some sort, and the barrel is getting a good polish.
Attachment 81309, 15 shots 50m, bench rest.
Attachment 81310, 10 more.
Perhaps a faster powder like 4227, I have used that (and sr4759) with good sucess in mine.
is that a capping breech loader?
Yea, you could be right, but I like one powder for all my rifle reloading and 3031 is good in 308,3030 and the Sharps , have tried A D I 2208 not to bad in the Sharps with medium loads . The main thing here is that it is a home made barrel and this is as good as it will get, maybe, every time I shoot it I`m polishing the barrel so it may improve over time. Good things take time, so more bullet casting, reloading, and range shooting and when my winter hunt comes around Ill be able to shoot the balls off a possy at 100m.
Hi 40mm, if you look back up the thread you will see 4 45-70 loaded cases, it`s a 1874 Sharps falling block, great fun.
Attachment 81320, The Quigley Sharps, 45-70.
Great! a shooting adventure after my own heart.
Is that how you are doing the test shooting, off the sticks like that, or off the bench?
What alloy are you using for your bullets?
How much are you compressing the black powder?
Are you using a card under the bullet?
Are you wiping the bore between shots when you shot those targets, or fired them in a row?
I would try a different softer lube for blackpowder, shoot a test with just straight Chefade see if that changes things.
One could try removing the ring on the nose for five rounds and see if that makes any difference.
O heck, #1 , Off the sticks/ no all shot off the bench, sticks was a shooting at the rams. #2, Lead alloy, pure lead, bit of linotype and tin. #3, Using 2f Swiss with small bit of compression . #4, Card on powder then bullet. #5, Just using blow tube between shots. #6, Make my own, bees wax, lanolin and olive oil mix, with a bit of red crayon, nice and soft. I don't think removing the ring would help, besides, it could be very painful, :XD: This is just my first try with my new 488gr bullets from my new mould and to see if my 1-20 twist will work, looks like it is, all neat round holes. But wait, there's more, have just borrowed a hollow base mould, 410gr so more testing.
well they will knock deer over at 50 ards no problem just go shoot a few will ya???? lol.
I am using Chefade, some beeswax and Canola oil, probably amounts to the same thing.Quote:
Originally Posted by homebrew.357
How much tin is in your mix?
How much difference do you think the card wad makes? I have tried it both ways and thought I could see a difference, but then could not repeat it.
I think a card wad over the powder helps seal the bullet base and also keeps the lube from getting into your powder charge . Always looks good when I shoot at 50m and have shot better ones with pp bullets and 420gr ones, but opens up at 100m, so will keep trying. MD, yes would love to try it on a deer or goats, but will have to put wheels on it to tow it around.
C H, just a small bit of tin, I have some pure tin and or a bit of solder will do it, helps fill out the mould.
Looking good doug
The real test will be the 1/2 size rams at 200:thumbsup:
Looking forward to seeing how those 405gn hollow base bullets go in your sharps certainly go awesome in my trapdoor